The foam handle of fitness equipment has uniform foam holes and is extremely elastic;
Soft, good elasticity, kink resistance and no deformation;
The grip product has excellent anti-slip performance and good resilience;
.Anti-aging, with higher tear strength and superior electrical properties;
The matte surface of the product is more conducive to perspiration
The amount of compression deformation is small, and the product color is rich and colorful.
The foam grips of fitness equipment are made of foam silicone raw materials and high-quality foam accessories. They are extruded through special processes. The products are colorful and have excellent visual effects. They are the best materials for contact with human skin. In comparison, the environmental protection performance is higher, the safety is more reliable, and the service life is longer. Silicone branch products have been strictly tested and can meet ROSH, FDA and other certifications;
serial number | project | standard | index |
1 | density | GB/T6363-2009 | 0.4~0.8g/cm3 |
2 | water absorption | QBT/T2669-2004 | ≤5% |
3 | Temperature use range: low temperature toughness |
ASTM D 1056 | ≤55°C |
4 | Temperature range of use: continuous use of the highest temperature |
SAE J 2236 | ≥200°C |
5 | Compression permanent change (22hrs70°C) | GB/T6669-2008 | ≤5% |
6 | Compression permanent change (22hrs100°C) | GB/T6669-2008 | ≤8% |
7 | Tensile strength (Mpa) | GB/T6344-2008 | ≥0.8Mpa |
8 | Elongation at break (%) | GB/T6344-2008 | ≥50% |
9 | Flame retardant grade (UL-94) | GB/T2408-2008 | HB~V-0 |
Flame Spread Index (Ls) | ASTM E 162 | ≤25 | |
Smoke density (Ds) | ASTM E 662 | ||
Tested in 4.0 minutes | ≤50 | ||
Tested in 1.5 minutes | ≤20 | ||
Pollutant gas level | SMP-800C | PASS |
The above performance products can be customized according to requirements
Regular products are shipped immediately after ordering, and special specifications are customized
Any color can be adjusted on demand
The surface of silicone products can be sprayed, screen printed, laser engraved, transferred